Technical

Stainless Steel


Grade
C (Max)
Mn (Max)
P (Max)
S (Max)
Si (Max)
Cr
Ni
Mo
Nitrogen (Max)
Cu/ Others
301
0.15
2.00
0.045
0.030
1.00
16.00 – 18.00
6.00 – 8.00
-
0.10
-
304
0.08
2.00
0.045
0.030
0.75
18.00 – 20.00
8.00- 10.50
-
0.10
-
304L
0.030
2.00
0.045
0.030
0.75
18.00 – 20.00
8.00- 12.00
-
0.10
-
310S
0.08
2.00
0.045
0.030
1.50
24.00- 26.00
19.00 – 22.00
-
-
-
316
0.08
2.00
0.045
0.030
0.75
16.00 – 18.00
10.00 – 14.00
2.00 – 3.00
0.10
-
316L
0.030
2.00
0.045
0.030
0.75
16.00 – 18.00
10.00 – 14.00
2.00 – 3.00
0.10
-
317
0.08
2.00
0.045
0.030
0.75
18.00 – 20.00
11.00 – 14.00
3.00 – 4.00
0.10
-
317L
0.030
2.00
0.045
0.030
0.75
18.00 – 20.00
11.00 – 15.00
3.00 – 4.00
0.10
-
321
0.08
2.00
0.045
0.030
0.75
17.00 – 19.00
9.00 – 12.00
-
0.10
Ti5 ( C + N ) Min or 0.70 max
347
0.08
2.00
0.045
0.030
0.75
17.00 – 19.00
9.00 – 13.00
-
-
Cb= 10x ( C Min ) or 1.00 Max
409
0.08
1.00
0.040
0.010
1.00
10.50 – 11.75
0.50
-
-
Ti= 6x (C+ N ) Min or 0.70 Max
409M
0.03
0.81.2
0.030
0.030
0.40.75
11.00- 12.00
1.5 max.
-
-
Ti= 6x (C) Min or 0.70 Max
410S
0.08
1.00
0.040
0.030
1.00
11.50- 13.50
0.60
-
-
-
410
0.15
1.00
0.040
0.030
1.00
11.50- 13.50
0.75
-
-
-
420
0.35
0.50
0.035
0.015
0.50
12.00 – 13.00
0.20.3
-
-
-
430
0.12
1.00
0.040
0.030
1.00
16.00 – 18.00
0.75
-
-
-
JSL AUS
0.08
7.08.0
0.070
0.030
0.75
15.50 – 16.50
4.25 – 4.75
-
-
0.9 – 1.10
JS- 203
0.08
9.2510.25
0.070
0.030
0.75
14.25 – 15.25
2.25 – 2.75
-
-
1.60- 2.0
301M
0.10
4.55.5
0.060
0.030
0.75
14.50 – 15.50
6.0 – 7.0
-
-
1.70- 1.90
* Thickness of 1.27mm & below will have elongation of 20% min.

Alloy Steel


Chemical Composition,%

Tensile Test

Designation
C max.
Si
P max
S max
Tensile Strength Kgf/mm2
Yield Point Kgf/mm2,min.
Elongation
Test Piece
%, min
IS 2002-1
0.18
.010-0.35
0.40
0.40
37-45
55
5.65/So
4/So
26
30
IS 2002-2A
0.20
0.10-0.35
0.050
0.050
42-50
50
5.65/So
4/So
25
29
IS 2002-2b
0.22
0.10-0.35
0.050
0.050
52-62
50
5.65/So
4/So
20
24

Kawasaki Specification [AG] Steel Plates for Galvanizing Pots


Chemical Composition,%

Tensile Test

Bend test

Designation
C    Si    Mn     P   S
Max       Max        Max
Yield Point      Tensile Strength
Kgf/mm2        Kgf/mm2.(N/mm2)
Elongation
%, Test Piece
Angle of Bend
Inside Radius
AG
0.09 tr.0.20-0.40 0.30 0.030
–                           –
–                  –

ASTM A 285-78 Pressure Vessel Plates Carbon Steel, Low – and Intermediate- Tensile Strength


Chemical Composition,%

Tensile Test*1

1. (i) Refer to  (1) for ASTM A 203

(ii) Refer to (2) for ASTM A 203

(iii) Refer to (4) for ASTM A 203.

Designation
C max
Mn max
P max
S max
Tensile Strength
ksi (MPa),
Yeild Strengh ksi(MPa),min.
Elongation,% min

GL=8 in.
GL=2 in

A 285 A
0.17
0.90
0.035
0.040
45-65 (310-450)
24(165)
27              30
A 285  B
0.22
0.90
0.035
0.040
50-70(385-485)
27(185)
25
28
A 285 C
0.28
0.90
0.035
0.040
55-75(380-515)
30(205)
23              27

Stainless Steel


Grade
Tensile
Strength Mpa, (Min)
Yield
Strength
Mpa, (Min)
%Age Elongation
in 50mm
gauge length min
Hardness (Max)
BHN
Rb
301
515
205
40
217
95
304
515
205
40
201
92
304L
485
170
40
201
92
310S
515
205
40
217
95
316
515
205
40
217
95
316L
485
170
40
217
95
317
515
205
35
217
95
317L
515
205
40
217
95
321
515
205
40
217
95
347
515
205
40
201
92
409
380
170
20
179
88
409M
430
275
20
187
90
410S
415
205
22
183
89
410
450
205
20
217
89
420
700( max )
-
15
217
95
430
450
205
22
183
89
JSL AUS
515
205
40
217
95
JS- 203
515
205
40
217
95
301M
515
205
40
217
95

Alloy Steel


Chemical Composition,%

Tensile Test

Designation
C max.
Si
P max
S max
Tensile Strength Kgf/mm2
Yield Point Kgf/mm2,min.
Elongation
Test Piece
%, min
IS 2002-1
0.18
.010-0.35
0.40
0.40
37-45
55
5.65/So
4/So
26
30
IS 2002-2A
0.20
0.10-0.35
0.050
0.050
42-50
50
5.65/So
4/So
25
29
IS 2002-2b
0.22
0.10-0.35
0.050
0.050
52-62
50
5.65/So
4/So
20
24

Stainless Steel


Nominal Broe
Outside Diameter
Schedule 5S
Schedule 10S
Schedule 40S
Schedule 80S
Schedule 160S
Schedule XXS
mm
INCH
mm
Wt mm
Weight (Kg/mt)
Wt
mm
Weight (Kg/mt)
Wt
mm
Weight (Kg/mt)
Wt
mm
Weight (Kg/mt)
Wt mm
Weight (Kg/mt)
Wt
mm
Weight (Kg/mt)
3
1/8
10.3
1.24
0.276
1.24
028
1.73
0.37
2.41
0.47
-
-
-
-
6
1/4
13.7
1.24
0.390
1.65
049
2.24
0.631
3.02
.0.80
-
-
-
-
10
3/8
17.1
1.24
0.490
1.65
0.63
2.31
0.845
3.20
1.10
-
-
-
-
15
1/2
21.3
1.65
0.800
2.11
1.00
2.77
1.27
3.75
1.62
4.75
1.94
7.47
2.55
20
3/4
26.7
1.65
1.03
2.11
1.28
2.87
1.68
3.91
2.20
5.54
2.89
7.82
3.63
25
1
33.4
1.65
1.30
2.77
2.09
3.38
2.50
4.55
3.20
6.35
4.24
9.09
5.45
32
1.1/4
42.2
1.65
1.65
2.77
2.70
3.56
3.38
4.85
4.47
6.35
5.61
9.70
7.77
40
1.1/2
48.3
1.65
1.91
2.77
3.11
3.68
4.05
5.08
5.41
7.14
7.25
10.16
9.54
50
2
60.3
1.65
2.40
2.77
3.93
3.91
5.44
5.54
7.48
8.74
11.1
11.07
13.44
65
2.1/2
73.0
2.11
3.69
3.05
5.26
5.16
8.63
7.01
11.4
9.53
14.9
14.2
20.39
80
3
88.9
2.11
4.51
3.05
6.45
5.49
11.30
7.62
15.2
11.1
21.3
15.24
27.65
100
4
114.3
2.11
5.84
3.05
8.36
6.02
16.07
8.56
22.3
13.49
33.54
17.12
41.03
125
5
141.3
2.77
9.47
3.40
11.57
6.55
21.8
9.53
31.97
15.88
49.11
19.05
57.43
150
6
168.3
2.77
11.32
3.40
13.84
7.11
28.3
10.97
42.7
18.2
67.56
21.95
79.22
200
8
219.1
2.77
14.79
3.76
19.96
8.18
42.6
12.7
64.6
23.0
111.2
22.23
107.8
250
10
273.1
3.40
22.63
4.19
27.78
9.27
60.5
12.7
96.0
28.6
172.4
25.40
155.15
300
12
323.9
3.96
31.25
4.57
36.00
9.52
73.88
12.7
132.0
33.32
238.76
25.40
186.97
350
14
355.6
3.96
34.36
4.78
41.3
11.13
94.59
19.05
158.08
35.71
281.70
-
-
400
16
406.4
4.19
41.56
4.78
47.29
12.7
123.30
21.41
203.33
40.46
365.11
-
-
450
18
457.2
4.19
46.80
4.78
53.42
14.27
155.80
23.8
254.36
45.71
466.40
-
-
500
20
508.0
4.78
59.25
5.54
68.71
15.09
183.42
26.19
311.2
49.99
564.68
-
-
600
24
609.6
5.54
82.47
6.35
94.45
17.48
255.41
30.96
442.08
59.54
808.22
-
-